Analysis of titanium nitrides precipitated during medium carbon steels solidification
Constantino Capurro, , Carlos Cicutti
Tenaris Siderca R&D Center, Steelmaking Department, J. Simini 250, 2804 Campana, Bs As, Argentina
Received 20 November 2017, Accepted 10 April 2018
Abstract

For certain applications, coarse titanium nitride (TiN) precipitates can be deleterious for the final properties of the material. Hence, in order to better understand the mechanisms involved in the generation of these precipitates, a characterization of the particles observed in steels with different titanium and nitrogen content was carried out. Samples from liquid steel (tundish), continuous casting billets and final product were evaluated using an Automatic Particle Analyzer (APA) coupled to a Scanning Electron Microscope (SEM). The location, frequency, size distribution and composition of the different particles observed were assessed. While only few TiN precipitates were observed in liquid steel samples, the density of this type of particles significantly increased in the continuous casting billets samples. Particles ranging from 1 to 10μm were mainly found in the interdendritic zones of the as-cast structure. The density of TiN particles observed in these samples did not change after re-heating and rolling operations. A microsegregation model previously developed was adapted to predict TiN precipitation during solidification. A reasonable agreement was found between model results and measured data. Results of this analysis confirmed that the precipitated fraction of TiN increases as the product of steel Ti and N contents rises.

Keywords
Titanium nitride, Solidification, Continuous casting, Microsegregation model
J Mater Res Technol 2018;7:342-9 DOI: 10.1016/j.jmrt.2018.04.010
Cookies Policy
x
To improve our services and products, we use cookies (own or third parties authorized) to show advertising related to client preferences through the analyses of navigation customer behavior. Continuing navigation will be considered as acceptance of this use. You can change the settings or obtain more information by clicking here.